 The intention of this specification is to outline the procedures for the application of Energy Seal Coatings for the purpose of coating SINGLE PLY ROOFING surfaces. These suggested specifications describe materials, methods and conditions necessary for the proper application of Energy Seal coatings. Actual application requirements are the responsibility of the installer.
 2.0 MATERIALS
All materials used shall be manufactured by and or approved by Advanced Coating Systems, Inc. Please refer to our product data sheets for technical specifications:
ACU-GLOSS - Acrylic elastomeric clear coat.
ACU-SHIELD - Acrylic elastomeric roof coating.
ACU-SHIELD:CERAMIC - Acrylic elastomeric ceramic roof coating.
ACU-CAULK:BG - Acrylic elastomeric brush grade caulk.
ACU-CAULK:FG - Acrylic flashing grade caulk.
ACU-PRIME ALL - Primer for non-metal or non-rusted metal surfaces.
ACU-TAC - Bonding Primer and Fabric Adhesive.
ACU-FABRIC:SB - Spunbound polyester reinforcing scrim.
Materials shall be delivered in their original, tightly sealed containers or unopened packages, all clearly labeled with the manufacturer's name, file number and lot numbers.
3.0 PREPARATION
Preparation shall include all requirements specified by Energy Seal Coatings, to ensure proper adhesion of the Energy Seal Coatings products to the existing substrate. New single-ply roofing surfaces must be allowed to cure a minimum of 90 days prior to application.
Preparation shall include but not limited to the following:
All unnecessary and non-functional equipment and debris shall be removed from the roof.
Substrate must be pressure-washed. A minimum working pressure of 3,000 psi shall be used to remove all dirt, dust, previous paints & coatings which are delaminating as well as waste products (oil, oil-based roof cements,solvents, grease, animal fats, etc). Use TSP (Tri Sodium Phosphate).
HVAC condensate drains shall be properly routed to roof drains to allow roof membrane and coatings to properly cure and dry.
Wet roof insulation and damaged membranes are to be removed and replaced as necessary to match existing specified material.
All wrinkles and blisters shall be mechanically removed. These areas should be detailed using ACU-FABRIC and ACU-TAC. Apply a thin layer of ACU-TAC on each area, roll out ACU-FABRIC into the wet coating and then apply a layer of ACU-TAC over the ACU-FABRIC. ACU-FABRIC should extend 6” around the repaired area. ACU-CAULK should be applied over the ACU-FABRIC to blend in the surface when the ACU-TAC has totally dried.
4.0 COATING APPLICATION
Examine substrate to receive roof coating. Do not proceed with installation of Energy Seal Coatings until
unsatisfactory conditions have been corrected in a manner acceptable to the manufacturer.
Entire roof shall be primed with ACU-PRIME ALL at a rate of 250 square feet per gallon. ACU-PRIME ALL must be allowed to cure for 24 hours.
To help stop leaks, all seams, penetrations and parapet walls are to be flashed using ACU-FABRIC and ACU-TAC. Apply a thin layer of ACU-TAC on each seam, roll out 6" ACU-FABRIC into the wet coating and then apply a layer of ACU-TAC over the ACU-FABRIC. The same procedure should be used on all parapet walls using 44" ACU-FABRIC with 20" running up the wall.
ACU-SHIELD roof coating is to be applied only after the ACU-PRIME ALL has thoroughly cured and dried for at least 24 hours. Recommended coverage is two coats (20 mils) on new roofs or three coats (30 mils) for aged older roofs. Contact Advanced Coating Systems for additional information.
Apply ACU-GLOSS clear acrylic coating (optional) at a rate of 250 square feet per gallon. ACU-GLOSS helps keep the surface clean thereby reducing maintenance costs.
Each coat must be allowed to cure for 24 - 48 hours depending on humidity and temperature. The roof is to be inspected for defects, flaws or holidays and repaired if necessary before a subsequent coat is applied.
5.0 APPLICATION RATES
5-year warranty: ACU-FLEX (2 gal./100 sq.ft.) - 1 primer, 2 finish coats (20 dry mils average).
10-year warranty: ACU-FLEX (3 gal./100 sq.ft. - 1 primer, 3 finish coats (30 dry mils average).
6.0 RESTRICTIONS / LIMITATIONS
This system is to be used only in conjunction with commonly accepted roofing standards but not limited to the following:
No application of materials shall commence during inclement weather or when precipitation is imminent. No thinning of materials permitted.
No materials are to be applied to wet, dirty or frozen surfaces.
No materials are to be applied at temperatures below 40°F.
No materials are to be applied at ambient temperatures above 100°F.
No materials are to be applied at relative humidity levels above 88%.
In conjunction with the final inspection, all debris, containers, materials and equipment are to be properly removed from the job site. Grounds are to be cleaned undamaged and acceptable to the owner.
Reflectivity of coatings may be reduced if roof surface is not cleaned on a regularly scheduled basis.
Ponding water areas must be repaired prior to any coating application so as to allow water to drain off the roof.
| |
 CAUTION: Do not apply within two hours of sunset, rain, fog or freezing temperatures. Energy Seal Coatings must be completely dry before exposing to water or foot traffic. Keep Energy Seal Coatings containers covered when not in use. Dispose of all containers in accordance with state and local environmental regulations. Keep away from children. If ingested, DO NOT induce vomiting. Call Physician immediately.
Our suggested installation specifications are based on information from laboratory and field testing which we believe to be reliable and correct.; however, accuracy and completeness of said tests are not guaranteed and should not be construed as a warranty, either expressed or implied. Since the use of the material is beyond manufacturer's control, buyer assumes all risk whatsoever as to their use or results obtained. We guarantee our products to conform to Advanced Coating Systems, Inc. quality control. Advanced Coating Systems, Inc. warrants only the standard quality of the material. Manufacturer's sole responsibility shall be to replace that portion of the Energy Seal Coatings product which proved defective.
|